Industrial MIM Parts
MIM Industrial Parts Gallery
MIM as the most cost-effective manufacturing way has widely application for industrial parts production. Our company has cooperated with thousands of partners for their special projects. Our main productions are micro-gears, drone metal parts, machinery components, and finally special design parts of pepper spray.
Micro Gear
- Material: Fe4Ni
- Size: 2.58mm×2.29mm
- Density: ≥7.55g/cm³
- Properties: Tensile strength ≥ 630 MPa, Yield strength ≥ 380 MPa, Hardness of 90HV10.
- Manufacturing process: Metal injection molding, Heart-treatment.
- Material: Fe4Ni
- Size: 1.22mm diameter
- Density: ≥7.55g/cm³
- Properties: Tensile strength ≥ 630 MPa, Yield strength ≥ 380 MPa, Hardness of 90HV10.
- Manufacturing process: Metal injection molding, Heart-treatment.
- Material: Fe4Ni
- Size: 5.67mm diameter
- Density: ≥7.55g/cm³
- Properties: Tensile strength ≥ 630 MPa, Yield strength ≥ 380 MPa, Hardness of 90HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Fe4Ni
- Size: 8.72mm diameter
- Density: ≥7.55g/cm³
- Properties: Tensile strength ≥ 630 MPa, Yield strength ≥ 380 MPa, Hardness of 90HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Fe4Ni
- Size: 5.00mm diameter
- Density: ≥7.55g/cm³
- Properties: Tensile strength ≥ 630 MPa, Yield strength ≥ 380 MPa, Hardness of 90HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 17-4PH
- Size: 18.47mm diameter
- Density: ≥7.65g/cm³
- Properties: Tensile strength ≥ 450 MPa, Yield strength≥140 MPa, Hardness of 300HV10.
- Manufacturing process: Metal injection molding, Electroplating.
- Material: Stainless steel 316L
- Size: 8.01mm×12.15mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Fe2Ni
- Size: 3.39mm diameter
- Density: ≥7.55g/cm³
- Properties: Tensile strength ≥ 260 MPa, Yield strength ≥ 150 MPa, Hardness of 90HV10.
- Manufacturing process: Metal injection molding, Heart-treatment.
Drone Parts
- Material: Stainless steel 316L
- Size: 63.54mm in whole
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding, Polishing, Chrome plating.
- Material: Stainless steel 316L
- Size: 13.84mm×12.9mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding, Polishing, Chrome plating.
- Material: Stainless steel 304
- Size: 16.22mm diameter, 3.5mm thickness
- Density: ≥7.8g/cm³
- Properties: Tensile strength ≥ 500 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding, Chrome plating.
- Material: Stainless steel 17-4PH
- Size: 18.85mm×14.39mm
- Density: ≥7.65g/cm³
- Properties: Tensile strength ≥ 450 MPa, Yield strength≥140 MPa, Hardness of 300HV10.
- Manufacturing process: Metal injection molding, PVD coating.
- Material: Stainless steel 17-4PH
- Size: 14.47mm×8.76mm
- Density: ≥7.65g/cm³
- Properties: Tensile strength ≥ 450 MPa, Yield strength≥140 MPa, Hardness of 300HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 17-4PH
- Size: 9.41mm
- Density: ≥7.65g/cm³
- Properties: Tensile strength ≥ 450 MPa, Yield strength≥140 MPa, Hardness of 300HV10.
- Manufacturing process: Metal injection molding, PVD coating.
- Material: Stainless steel 17-4PH
- Size: 10.56mm×8.10mm
- Density: ≥7.65g/cm³
- Properties: Tensile strength ≥ 450 MPa, Yield strength≥140 MPa, Hardness of 300HV10.
- Manufacturing process: Metal injection molding, PVD coating.
- Material: Stainless steel 316L
- Size: 6.10mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, PVD coating.
Pepper Spray Parts
- Material: Fe2Ni/Fe8Ni
- Size: 30.74mm×59.25mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding, Heat treatment, Chemical plating.
- Material: Fe2Ni/Fe8Ni
- Size: 34.4mm×24.27mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding, Heat treatment, Chemical plating.
- Material: Fe2Ni/Fe8Ni
- Size: 7.03mm×38.8mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding, Heat treatment, Chemical plating.
- Material: Fe2Ni/Fe8Ni
- Size: 26.14mm×19.76mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding, Heat treatment, Chemical plating.
Machinery Components
- Material: Stainless steel 316L
- Size: 6.84mm×53.04mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 3.91mm×49.55mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 7.98mm×58.26mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding, Polishing, Wire drawing.
- Material: Stainless steel 316L
- Size: 8.47mm×7.98mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 20.17mm×48.86mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 18.4mm×28.56mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 16.84mm×29.58mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 14.05mm×13.48mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.