Electronic MIM Parts
MIM Mobilephone Parts Gallery
Our main MIM parts are: SIM cardholder, slot tray, metal mobile-phone button. We also produce cable and cords holder for notebook and computer.
Mobilephone Button
- Material: Stainless steel 316L
- Size: 2.44mm×14.16mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 13.94mm×38.77mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 13.94mm×38.77mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 9.18mm×5.69mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, PVD coating.
- Material: Stainless steel 316L
- Size: 9.79mm×3.28mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
Mobilephone Camera Parts
- Material: Stainless steel 316L
- Size: 5.00mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Fe04Ni
- Size: 6.75mm×5.03mm
- Density: ≥7.55g/cm³
- Properties: Tensile strength ≥ 630 MPa, Yield strength ≥ 380 MPa, Hardness of 90HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 7.33mm×4.82mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Fe04Ni
- Size: 3.01mm×4.07mm
- Density: ≥7.55g/cm³
- Properties: Tensile strength ≥ 630 MPa, Yield strength ≥ 380 MPa, Hardness of 90HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Fe4Ni
- Size: 2.50mm
- Density: ≥7.55g/cm³
- Properties: Tensile strength ≥ 630 MPa, Yield strength ≥ 380 MPa, Hardness of 90HV10.
- Manufacturing process: Metal injection molding, Heat treatment.
- Material: Fe4Ni
- Size: 1.40mm
- Density: ≥7.55g/cm³
- Properties: Tensile strength ≥ 630 MPa, Yield strength ≥ 380 MPa, Hardness of 90HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
Cable&Cord Container
- Material: Stainless steel 316L
- Size: 7.01mm×10.22mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 6.34mm×14.51mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 13.89mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 18.81mm×31.09mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size:18.78mm×20.18mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size: 7.18mm×8.05mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding, PVD coating.
- Material: Stainless steel 316L
- Size:9.12mm×5.50mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding, Passivation.
- Material: Stainless steel 316L
- Size: 7.98mm×8.47mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding.
- Material: Stainless steel 316L
- Size:63.26mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding, Anodizing.
- Material: Stainless steel 316L
- Size: 48.75mm×13.79mm
- Density: ≥7.8g/cm³
- Properties: Tensile strength of 510 MPa, Yield strength≥180 MPa, Hardness of 120HV10.
- Manufacturing process: Metal injection molding, Magnetic grinding, Passivation.